KAPRA Silicone ZA22 THIXO BODY A+B
  • KAPRA Silicone ZA22 THIXO BODY A+B
keyboard_arrow_up keyboard_arrow_down

KAPRA Silicone ZA22 THIXO BODY A+B

content Unit price Buy
1 + 1 kg
€92.02
10 + 10 kg
€755.46


All prices incl. VAT, plus shipping costs.
For deliveries to countries other than Germany
the final prices may change in the checkout.
MORE INFO

Silicone rubbr RTV EC22 for skin contact. Two-component silicone with polyaddition curing. For body moulding and mask making. For very detailed moulding.

For fast and very detailed moulding, e.g. of skin surfaces.

Paste-like, spreadable silicone that vulcanises at room temperature and can also be used for vertical work. Exceptional non-stick properties. Very suitable for special effects. RTV EC22 moulds can be filled with many materials, e.g. plaster, wax and synthetic resins. Several castings are possible with one mould. Talcum powder can be used as a release agent.

APPLICATION:

Weigh component A (pink) and component B (white) precisely in different containers and stir carefully and thoroughly in equal proportions by weight (100:100) to form a homogeneously coloured mass. Ensure that no residues remain in the weighing containers - a deviation from the mixing ratio of more than 5 % can change the vulcanisation. Process the silicone compound immediately after mixing.

The silicone cures at room temperature. Changing the room temperature can shorten or lengthen the processing time, while also changing the curing time: at 40 °C, the processing time and curing time are roughly halved; at 4 °C, the processing time is doubled and the curing time is approximately three times longer - in relation to the processing and curing time at a room temperature of 23 °C.

If skin surfaces are to be moulded with the silicone, apply Vaseline beforehand if necessary to protect fine hairs.

TECHNICAL DATA:

Colour component A (base): pink
Colour component B (crosslinker): white
Specific density: 1.14 g/cm³
Mixing ratio (weight): 1:1
Mixing time at 23 °C: 1 min.
Processing time (pot life) at 23 °C: 10 min.
Start of curing at 23 °C: 25 min.
Shore A hardness after 24 hours: 22 ± 2
Breaking load: 2.5 ± 0.3 N/mm²
Elongation at break: 360 ± 20 %
Tear strength: 14 ± 1 N/mm
Dimensional change after 24 hours: 0.05 %
Complete vulcanisation at 23 °C: 24 hours

The curing of polyaddition silicones can be impaired by
- Latex glove
- Salts of heavy metals
- Amines
- Sulphur and sulphur derivatives
- Hardeners for epoxy resin

Classification according to Regulation (EC) No. 1272/2008: The product is not classified as hazardous according to the GHS/CLP guidelines and does not require labelling.

Zhermack Silicone ZA 22 Thixo Body

EUH210: Safety data sheet available on request.

cross-linking
Polyaddition

SHD_A_Zhermack Silikon ZA 22 Thi

Download (606.95KB)


SHD_B_Zhermack Silikon ZA 22 Thi

Download (602.93KB)


TDS_Zhermack Silikon ZA 22 Thixo

Download (537.67KB)


Accessories Products

Related Products ( 8 other products in the same category )

New Account Register

Already have an account? Log in here.